All Flexible Foam Insulation are engineered and manufactured for HVAC and other industrial applications. With closed cell structure Flexible Foam insulations effectively retard heat flow and prevent condensation when properly installed. The environmental friendly materials are manufactured without the use of CFCa€?s, HFCa€?s or HCFCa€?s. They are also formaldehyde free, low VOCs, fiber free, dust free and resistant to mold and mildew.
Our Flexible Foam Sheet & pipe outperforms in fire resistance, water vapor permeability and thermal conductivity features. Its unique formulation makes it an ideal choice for extreme design conditions such as high humidity and low line temperature.
Our Flexible Foam Sheet & pipe have excellent fire performance meeting the Class 0 & Class 1 accordance with BS 476 Part 6 & Part 7.
KEY PERFORMANCE MEASURES
?1?50?°C to ?1?105?°C temperature range
1.16?—10-13Kg/MPa water vapor transmission
0.039W/mK thermal l conductivity values
Fire performance with Class 0 & Class 1
APPLICATIONS
Flexible Foam Sheet & pipe insulation is used to retard heat transmission and control condensation from chilled-water and refrigeration systems. It also efficiently reduces heat transfer for hot-water plumbing and liquid-heating and dual-temperature piping. It is ideal for applications in: Ductwork, Large piping and fittings, Tanks, Vessels, Curved and irregular surfaces and all types of fitting covers It is installed using our Glue 520, 520B or 520LV Adhesive. For application to large, flat or curved metal surfaces full adhesive coverage attachment is applied.
Technic Information
|
Item |
Unit |
Index |
Standard |
|
Working temperature |
a?? |
-50-110 |
- |
|
Density |
Kg/m3 |
40-80 |
GB/T-6343 |
|
Water absorption ratio in vacuum |
% |
a‰¤10 |
GB/T17794 |
|
Thermal conductivity |
W/(m?·k) |
a‰¤0.032 (-20a??) |
GB/T10294 |
|
a‰¤0.034(0a??) |
GB/T10296 |
|
a‰¤0.039(40a??) |
DIN 52612, DIN52613 |
|
Flammability |
- |
B1 |
GB 8624 |
|
V0 |
UL 94 |
|
1 |
BS 476 part 7 |
|
SDR |
- |
a‰¤65 |
GB/T8627 |
|
Noxiousness of smoke |
- |
Safe AZ3 |
GA 132 |
|
Water vapor permeability |
Coefficient |
Kg(m?·s?·pa) |
a‰¤1.96*10-14 |
DIN 52615, BS EN ISO9346
BS 4370 part 2, GB/T17146 |
|
Factor |
- |
a‰?10000 |
|
Oxygen Index |
% |
K0a‰?40
|
GB/T 2406, ISO 4589 |
|
K1a‰?35 |
|
Dimension stability |
% |
a‰¤10 |
GB 8811 |
|
Anti-Ozone 200h
200h |
- |
No cracking |
GB/T 7762, GB/T 9571
GB/T9571 |
|
Aging resistance 150h |
Slightly crumpling, no cracks, no pin holes, no deforming |
GB/T16259 |
|
Crack resistance |
N/cm |
a‰?3 |
GB/T10808 |
|
Compression resilience ratio
Compression Ratio 50%
Compression time 72h |
% |
a‰?70 |
GB/T6669 |
|
Thickness |
mm |
6,9,10,15,20,25,30,35,etc |
- |
|
Standard width |
m |
1 |
- |
|
Standard length |
m |
10,20 |
- |
Reference thickness for different temperature
|
Tube size |
Temperature |
|
50a?‰(10a??) |
35a?‰(2a??) |
0a?‰(-18a??) |
-20a?‰(-29a??) |
|
For standard condition: Max temperature: 29a??, Max humidity: 70% |
|
Inner-diameter 10mm-28mm |
10mm |
13mm |
19mm |
25mm |
|
Inner-diameter 28mm-54mm |
10mm |
13mm |
25mm |
25mm |
|
Inner-diameter 54mm-65mm |
10mm |
13mm |
25mm |
32mm |
|
Inner-diameter 65mm-168mm |
13mm |
19mm |
25mm |
32mm |
|
For gentle condition: Max temperature: 27a??, Max humidity: 50% |
|
Inner-diameter 10mm-65mm |
10mm |
10mm |
13mm |
19mm |
|
Inner-diameter 65mm-168mm |
13mm |
13mm |
13mm |
19mm |
|
For tough condition: Max temperature: 32a??, Max humidity: 80% |
|
Inner-diameter 10mm-40mm |
19mm |
25mm |
38mm |
38mm |
|
Inner-diameter 40mm-90mm |
19mm |
25mm |
38mm |
44mm |
|
Inner-diameter 90mm-168mm |
19mm |
25mm |
38mm |
50mm |
|
|
|
|
|
|
1, For temperature over 32a??/humidity over 80%, can check with our engineer for recommendation.
2,For thickness over 25mm, multiple layer could be used 3,Only for your reference, users can chose different thickness according to their onw situation |